| Wingi: | |
|---|---|
ZC-3241
I tem | Un | Njia ya mtihani | S Tandard V Aue | Kawaida Thamani | |
Nguvu tensile | MPA | IEC 60811- 1- 1 | ≥ 13.5 | 18.5 | |
Elongation wakati wa mapumziko | % | ≥ 350 | 465 | ||
Athari za utendaji wa kukumbatia@-76c | Nambari ya kutofaulu | Sehemu | ASTM D746 | ≤15/30 | 0/30 |
Baada ya kuzeeka @135c, 168h | Tofauti ya nguvu ya nguvu | % | IEC 60811- 1-2 | ± 20 | +7 |
Kuvunja Tofauti ya Elongation | % | ± 20 | +1 | ||
Kuongeza moto@200c, 0.2mpa, 15min | Elongation chini ya mzigo | % | IEC 60811-2- 1 | ≤80 | 50 |
Marekebisho ya kudumu | % | ≤5 | 0 | ||
Sababu ya dielectric discipation@20c, 50Hz | － | IEC 60250 | ≤0.001 | 0.0003 | |
Jamaa dielectric mara kwa mara@20c, 50Hz | － | ≤ 2.35 | 2.25 | ||
Nguvu ya dielectric@20c | Mv/m | IEC 60243- 1 | ≥ 25 | 37 | |
Kiasi cha resistation@20c | Ω · m | IEC 60093 | ≥ 5 × 1013 | 6 × 1014 | |
Mazingira ya Upinzani wa Mazingira F50 | hr | IEC 811-4-1 | ≥ 1000 | Kupita | |
Upinzani wa hali ya hewa wa kuzeeka (baada ya siku42) | Tofauti ya nguvu ya nguvu | % | GB/T 14049 | ± 30 | - 19 |
Kuvunja Tofauti ya Elongation | % | ± 30 | -25 | ||
Upinzani wa kuzeeka wa hali ya hewa (baada ya siku 21) | Tofauti ya nguvu ya nguvu | % | ± 15 | -9 | |
Kuvunja Tofauti ya Elongation | % | ± 15 | - 11 | ||
Pendekeza kwa extruder maalum ya polyethilini. Uwiano wa kuchora ni kutoka 18: 1 hadi 25: 1 na vifaa vingine vinahitaji kubadilishwa kulingana na hali.
Eneo | Sehemu ya kulisha | Sehemu ya compression | Sehemu ya homogenization | Sehemu ya mfano |
Kiwango cha joto c | 160- 180 | 180-200 | 200-220 | 220-230 |
- Juu ya joto ni kwa kumbukumbu tu.
Kwa safu ya jumla ya insulation ya cable (1 mm kwa unene) inaweza kuunganishwa baada ya kuoga katika 90c juu ya maji ya moto kwa masaa 4. Ikiwa unene wa insulation ni kubwa, inapaswa kuwa sawa kupanua wakati wa kuoga. Kupanuliwa na 1mm/4h au kupanua wakati kulingana na joto maalum kwa data iliyopanuliwa.
Weka kwenye joto la kawaida ; Mazingira ya uhifadhi yanapaswa kuwa safi, kavu na hewa; Matumizi bora ndani ya sita
miezi kutoka tarehe ya uzalishaji; Tafadhali tumia masaa 16 baada ya begi kufunguliwa.
Ufungashaji: 25kg/begi (mifuko ya alumini-sugu ya aluminium + mifuko ya karatasi ya mchanganyiko).
Uhifadhi: Hifadhi katika mazingira safi, kavu, yenye hewa kwa joto la kawaida. Tumia ndani ya miezi 6 ya uzalishaji; Tumia ndani ya masaa 16 baada ya kufunguliwa.
I tem | Un | Njia ya mtihani | S Tandard V Aue | Kawaida Thamani | |
Nguvu tensile | MPA | IEC 60811- 1- 1 | ≥ 13.5 | 18.5 | |
Elongation wakati wa mapumziko | % | ≥ 350 | 465 | ||
Athari za utendaji wa kukumbatia@-76c | Nambari ya kutofaulu | Sehemu | ASTM D746 | ≤15/30 | 0/30 |
Baada ya kuzeeka @135c, 168h | Tofauti ya nguvu ya nguvu | % | IEC 60811- 1-2 | ± 20 | +7 |
Kuvunja Tofauti ya Elongation | % | ± 20 | +1 | ||
Kuongeza moto@200c, 0.2mpa, 15min | Elongation chini ya mzigo | % | IEC 60811-2- 1 | ≤80 | 50 |
Marekebisho ya kudumu | % | ≤5 | 0 | ||
Sababu ya dielectric discipation@20c, 50Hz | － | IEC 60250 | ≤0.001 | 0.0003 | |
Jamaa dielectric mara kwa mara@20c, 50Hz | － | ≤ 2.35 | 2.25 | ||
Nguvu ya dielectric@20c | Mv/m | IEC 60243- 1 | ≥ 25 | 37 | |
Kiasi cha resistation@20c | Ω · m | IEC 60093 | ≥ 5 × 1013 | 6 × 1014 | |
Mazingira ya Upinzani wa Mazingira F50 | hr | IEC 811-4-1 | ≥ 1000 | Kupita | |
Upinzani wa hali ya hewa wa kuzeeka (baada ya siku42) | Tofauti ya nguvu ya nguvu | % | GB/T 14049 | ± 30 | - 19 |
Kuvunja Tofauti ya Elongation | % | ± 30 | -25 | ||
Upinzani wa kuzeeka wa hali ya hewa (baada ya siku 21) | Tofauti ya nguvu ya nguvu | % | ± 15 | -9 | |
Kuvunja Tofauti ya Elongation | % | ± 15 | - 11 | ||
Pendekeza kwa extruder maalum ya polyethilini. Uwiano wa kuchora ni kutoka 18: 1 hadi 25: 1 na vifaa vingine vinahitaji kubadilishwa kulingana na hali.
Eneo | Sehemu ya kulisha | Sehemu ya compression | Sehemu ya homogenization | Sehemu ya mfano |
Kiwango cha joto c | 160- 180 | 180-200 | 200-220 | 220-230 |
- Juu ya joto ni kwa kumbukumbu tu.
Kwa safu ya jumla ya insulation ya cable (1 mm kwa unene) inaweza kuunganishwa baada ya kuoga katika 90c juu ya maji ya moto kwa masaa 4. Ikiwa unene wa insulation ni kubwa, inapaswa kuwa sawa kupanua wakati wa kuoga. Kupanuliwa na 1mm/4h au kupanua wakati kulingana na joto maalum kwa data iliyopanuliwa.
Weka kwenye joto la kawaida ; Mazingira ya uhifadhi yanapaswa kuwa safi, kavu na hewa; Matumizi bora ndani ya sita
miezi kutoka tarehe ya uzalishaji; Tafadhali tumia masaa 16 baada ya begi kufunguliwa.
Ufungashaji: 25kg/begi (mifuko ya alumini-sugu ya aluminium + mifuko ya karatasi ya mchanganyiko).
Uhifadhi: Hifadhi katika mazingira safi, kavu, yenye hewa kwa joto la kawaida. Tumia ndani ya miezi 6 ya uzalishaji; Tumia ndani ya masaa 16 baada ya kufunguliwa.